SPESIFIKASI STANDAR TABUNG COIL STAINLESS STEEL
Tabung melingkar baja tahan karat 321 6*1mm
| Standar | ASTM A213 (Dinding Rata-Rata) dan ASTM A269 |
| Diameter Luar Tabung Kumparan Stainless Steel | 1/16” hingga 3/4″ |
| Ketebalan Tabung Kumparan Stainless Steel | .010″ Hingga .083” |
| Nilai Tabung Kumparan Stainless Steel | SS 201, SS 202, SS 304, SS 304L, SS 309, SS 310, SS 316, SS 316L, SS 317L, SS 321, SS 347, SS 904L |
| Ukuran Rnage | 5/16, 3/4, 3/8, 1-1/2, 1/8, 5/8, 1/4, 7/8, 1/2, 1, 3/16 inci |
| Kekerasan | Mikro dan Rockwell |
| Toleransi | D4/T4 |
| Kekuatan | Meledak dan Tarik |
KELAS SETARA TABUNG COIL STAINLESS STEEL
Tabung melingkar baja tahan karat 321 6*1mm
| STANDAR | WERKSTOFF NR. | UNS | JIS | BS | gost | AFNOR | EN |
|---|---|---|---|---|---|---|---|
| SS 304 | 1.4301 | S30400 | SUS 304 | 304S31 | 08Х18Н10 | Z7CN18‐09 | X5CrNi18-10 |
| SS 304L | 1.4306 / 1.4307 | S30403 | SUS 304L | 3304S11 | 03Х18Н11 | Z3CN18‐10 | X2CrNi18-9 / X2CrNi19-11 |
| SS 310 | 1.4841 | S31000 | SUS 310 | 310S24 | 20Ch25N20S2 | – | X15CrNi25-20 |
| SS 316 | 1.4401 / 1.4436 | S31600 | SUS 316 | 316S31 / 316S33 | – | Z7CND17‐11‐02 | X5CrNiMo17-12-2 / X3CrNiMo17-13-3 |
| SS 316L | 1.4404 / 1.4435 | S31603 | SUS 316L | 316S11 / 316S13 | 03Ch17N14M3 / 03Ch17N14M2 | Z3CND17‐11‐02 / Z3CND18‐14‐03 | X2CrNiMo17-12-2 / X2CrNiMo18-14-3 |
| SS 317L | 1.4438 | S31703 | SUS 317L | – | – | – | X2CrNiMo18-15-4 |
| SS 321 | 1.4541 | S32100 | SUS 321 | – | – | – | X6CrNiTi18-10 |
| SS 347 | 1,4550 | S34700 | SUS 347 | – | 08Ch18N12B | – | X6CrNiNb18-10 |
| SS 904L | 1.4539 | N08904 | SUS 904L | 904S13 | STS 317J5L | Z2 NCDU 25-20 | X1NiCrMoCu25-20-5 |
KOMPOSISI KIMIA TABUNG COIL SS
Tabung melingkar baja tahan karat 321 6*1mm
| Nilai | C | Mn | Si | P | S | Cr | Mo | Ni | N | Ti | Fe | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Tabung Kumparan SS 304 | menit. | 18.0 | 8.0 | |||||||||
| maks. | 0,08 | 2.0 | 0,75 | 0,045 | 0,030 | 20.0 | 10.5 | 0,10 | ||||
| Tabung Kumparan SS 304L | menit. | 18.0 | 8.0 | |||||||||
| maks. | 0,030 | 2.0 | 0,75 | 0,045 | 0,030 | 20.0 | 12.0 | 0,10 | ||||
| Tabung Kumparan SS 310 | 0,015 maks | 2 maks | 0,015 maks | 0,020 maks | 0,015 maks | 24.00 26.00 | 0,10 maks | 19.00 21.00 | 54,7 menit | |||
| Tabung Kumparan SS 316 | menit. | 16.0 | 2.03.0 | 10.0 | ||||||||
| maks. | 0,035 | 2.0 | 0,75 | 0,045 | 0,030 | 18.0 | 14.0 | |||||
| Tabung Kumparan SS 316L | menit. | 16.0 | 2.03.0 | 10.0 | ||||||||
| maks. | 0,035 | 2.0 | 0,75 | 0,045 | 0,030 | 18.0 | 14.0 | |||||
| Tabung Kumparan SS 317L | 0,035 maks | 2,0 maks | 1,0 maks | 0,045 maks | 0,030 maks | 18.00 20.00 | 3,00 4,00 | 11.00 15.00 | 57,89 menit | |||
| Tabung Kumparan SS 321 | 0,08 maks | 2,0 maks | 1,0 maks | 0,045 maks | 0,030 maks | 17.00 19.00 | 9.00 12.00 | 0,10 maks | 5(C+N) 0,70 maks | |||
| Tabung Kumparan SS 347 | 0,08 maks | 2,0 maks | 1,0 maks | 0,045 maks | 0,030 maks | 17.00 20.00 | 9.0013.00 | |||||
| Tabung Kumparan SS 904L | menit. | 19.0 | 4.00 | 23.00 | 0,10 | |||||||
| maks. | 0,20 | 2.00 | 1,00 | 0,045 | 0,035 | 23.0 | 5.00 | 28.00 | 0,25 | |||
SIFAT MEKANIK KOIL STAINLESS STEEL
Tabung melingkar baja tahan karat 321 6*1mm
| Nilai | Kepadatan | Titik lebur | Daya tarik | Kekuatan Hasil (Offset 0,2%) | Pemanjangan |
|---|---|---|---|---|---|
| Tabung Kumparan SS 304/ 304L | 8,0 gram/cm3 | 1400 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35% |
| Tabung Kumparan SS 310 | 7,9 gram/cm3 | 1402 °C (2555 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 40% |
| Tabung Kumparan SS 306 | 8,0 gram/cm3 | 1400 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35% |
| Tabung Kumparan SS 316L | 8,0 gram/cm3 | 1399 °C (2550 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35% |
| Tabung Kumparan SS 321 | 8,0 gram/cm3 | 1457 °C (2650 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35% |
| Tabung Kumparan SS 347 | 8,0 gram/cm3 | 1454 °C (2650 °F) | Psi 75000 , MPa 515 | Psi 30000 , MPa 205 | 35% |
| Tabung Kumparan SS 904L | 7,95 gram/cm3 | 1350 °C (2460 °F) | Psi 71000 , MPa 490 | Psi 32000 , MPa 220 | 35% |